DM02 Hot slip shrink film
Its advantage is excellent thermal slip performance. The hot surface of a film that is not hot slip typically causes sticking after shrinking at high temperatures, which makes it difficult to put the packages together. DM02 is the best choice to avoid this difficulty. The DM02 performs very well on a full-speed packaging machine. In addition to the thermal slip properties, it has all the good properties of DM01.
Main Parameter Data |
| Product |
DM02 HOT SLIP SHRINK FILM |
| Property |
Unit |
Test Method |
Representative Value |
| Physical Property |
| Thickness |
Micron |
|
10 / 12.5 |
15 |
19 |
25 |
| Tensile Property (MD/TD) |
| Tensile Strength |
N/mm2 |
ASTM-882 |
115/115 |
115/115 |
115/115 |
115/115 |
| Elongation at Break |
% |
ASTM-882 |
105/110 |
110/110 |
110/110 |
115/110 |
| Seal Strength |
g/cm3 |
Internal Method |
611 |
872 |
1025 |
1252 |
| N/mm2 |
42 |
58 |
54 |
51 |
| Tear Propagation |
g/cm3 |
ASTM-D1938 |
11 |
14 |
16 |
24 |
| COF film to film |
Adim |
ASTM-D1894 |
0.15 |
0.15 |
0.15 |
0.15 |
| Free Shrink at 130¡æ |
% |
ASTM-D2732 |
70/70 |
70/70 |
70/70 |
70/70 |
| Optical Property |
| Haze |
% |
ASTM-D1003 |
1.2 |
1.4 |
1.9 |
2.4 |
| Gloss |
photoc |
ASTM-D2457 |
140 |
143 |
148 |
148 |
| Dimension Specification |
| Thickness |
Micron |
10 / 12.5 |
15 |
19 |
25 |
| Width |
mm |
200--1600 |
| Length /roll |
S/S(single layer) |
3200m |
2665m |
2135m |
1600m |
| C/F(center fold) |
1600m |
1332m |
1067m |
800m |
|
Values listed are average test values to be used for information purposes, subject to possible variations.
Products are to be stored in dry conditions below 35 deg. Cent. |